　　Naphthalene, as an important organic chemical raw material, is widely used in various fields such as medicine, dyes, plastics, etc. Understanding the corrosiveness of refined naphthalene in industrial production and storage processes is crucial for ensuring equipment safety, extending service life, and ensuring production safety. The corrosiveness of refined naphthalene is not a single characteristic, but is influenced by multiple factors and presents complex manifestations.

　　一、精萘的理化性質基礎

　　1、 The Physical and Chemical Properties of Naphthalene

　　精萘（CH）是萘經(jīng)過升華提純后的產(chǎn)物，為白色結晶性粉末，具有特殊的氣味，在常溫常壓下較為穩(wěn)定。其熔點約為 80.2℃，沸點 218℃，不溶于水，易溶于有機溶劑如乙醇、乙醚等 。從化學結構來看，精萘具有稠環(huán)芳烴的特性，分子結構相對穩(wěn)定，但在特定條件下，其化學性質會發(fā)生變化，從而可能引發(fā)腐蝕現(xiàn)象。

　　Naphthalene (CH) is a white crystalline powder obtained by sublimation purification of naphthalene, with a special odor and relatively stable at room temperature and pressure. Its melting point is about 80.2 ℃ and boiling point is 218 ℃. It is insoluble in water but easily soluble in organic solvents such as ethanol and ether. From a chemical structure perspective, naphthalene has the characteristics of polycyclic aromatic hydrocarbons, with a relatively stable molecular structure. However, under specific conditions, its chemical properties may change, which may lead to corrosion.

　　二、精萘對不同材料的腐蝕表現(xiàn)

　　2、 Corrosion behavior of refined naphthalene on different materials

　　（一）金屬材料

　?。?） Metal materials

　　精萘對大多數(shù)金屬的腐蝕性相對較弱。在常溫干燥環(huán)境中，精萘與金屬如鐵、銅、鋁等接觸時，一般不會發(fā)生明顯的化學反應和腐蝕現(xiàn)象。這是因為精萘本身的化學活性在常規(guī)條件下并不足以直接與金屬發(fā)生強烈的氧化還原反應。然而，當環(huán)境中存在水分時，情況會有所不同。水分可以作為電解質，在精萘與金屬表面形成微小的原電池，促使金屬發(fā)生電化學腐蝕 。

　　Naphthalene has relatively weak corrosiveness to most metals. In a dry environment at room temperature, refined naphthalene generally does not undergo significant chemical reactions or corrosion when in contact with metals such as iron, copper, aluminum, etc. This is because the chemical activity of naphthalene itself is not sufficient to directly undergo strong redox reactions with metals under conventional conditions. However, when there is moisture in the environment, the situation will be different. Water can act as an electrolyte, forming tiny primary cells on the surface of refined naphthalene and metal, promoting electrochemical corrosion of the metal.

　　此外，某些活性較強的金屬，如鋅、鎂等，在高溫且存在精萘蒸汽的環(huán)境下，可能會與精萘發(fā)生化學反應。精萘分子中的芳環(huán)結構在高溫下可能與金屬發(fā)生絡合或取代反應，導致金屬表面被侵蝕，出現(xiàn)腐蝕坑洞或表面剝落現(xiàn)象。不過，這種情況在實際應用中相對較少，通常需要特定的高溫和長時間接觸條件。

　　In addition, certain highly reactive metals such as zinc, magnesium, etc. may undergo chemical reactions with naphthalene at high temperatures and in the presence of naphthalene vapor. The aromatic ring structure in naphthalene molecules may undergo complexation or substitution reactions with metals at high temperatures, leading to corrosion of the metal surface, resulting in corrosion pits or surface peeling. However, this situation is relatively rare in practical applications and usually requires specific high temperature and long-term contact conditions.

　　（二）非金屬材料

　?。?） Non metallic materials

　　塑料與橡膠：精萘對部分塑料和橡膠材料具有一定的腐蝕性。由于精萘易溶于有機溶劑，而一些塑料和橡膠在化學結構上與有機溶劑存在相似性，精萘會滲透到塑料或橡膠內(nèi)部，導致其溶脹、變形甚至開裂 。例如，聚氯乙烯（PVC）材質的容器在長期接觸精萘后，會出現(xiàn)變軟、表面發(fā)黏的現(xiàn)象；天然橡膠制品與精萘接觸，橡膠的彈性會逐漸喪失，變得硬脆。因此，在儲存和運輸精萘時，應避免使用這類對精萘耐受性差的塑料和橡膠材料。

　　Plastic and rubber: Naphthalene has a certain corrosiveness to some plastic and rubber materials. Due to the solubility of naphthalene in organic solvents, and the chemical similarity between some plastics and rubber and organic solvents, naphthalene can penetrate into the interior of plastics or rubber, causing swelling, deformation, and even cracking. For example, containers made of polyvinyl chloride (PVC) material may become soft and have a sticky surface after long-term exposure to naphthalene; When natural rubber products come into contact with refined naphthalene, the elasticity of the rubber will gradually lose and become hard and brittle. Therefore, when storing and transporting refined naphthalene, the use of plastic and rubber materials with poor tolerance to refined naphthalene should be avoided.

　　木材：木材主要由纖維素、半纖維素和木質素等組成，精萘對木材的腐蝕性較小。但在潮濕環(huán)境下，精萘可能會吸附在木材表面，隨著時間推移，會使木材的顏色發(fā)生變化，出現(xiàn)泛黃或發(fā)黑現(xiàn)象，同時木材的物理性能也會受到一定影響，強度有所下降 。不過，這種腐蝕作用相對緩慢，通常不會對木材結構造成快速且嚴重的破壞。

　　Wood: Wood is mainly composed of cellulose, hemicellulose, and lignin, and refined naphthalene has less corrosiveness to wood. But in humid environments, refined naphthalene may adsorb on the surface of wood, and over time, it can cause the color of the wood to change, resulting in yellowing or blackening. At the same time, the physical properties of the wood will also be affected to some extent, and the strength will decrease. However, this corrosion process is relatively slow and usually does not cause rapid and severe damage to the wood structure.